Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.
Scientific Reports volume 13, Article number: 12887 (2023 ) Cite this article 48v Supercapacitor
Activated carbons (ACs) were developed from palm petiole via a new eco-friendly method composed of highly diluted H2SO4 hydrothermal carbonization and low-concentration KOH-activating pyrolysis followed by gamma-induced surface modification under NaNO3 oxidizing environment. The prepared graphitic carbons were subsequently used as an active material for supercapacitor electrodes. The physiochemical properties of the ACs were characterized using field emission scanning electron microscope–energy dispersive X-ray spectroscopy, N2 adsorption/desorption isotherms with Brunauer–Emmett–Teller surface area analysis, Fourier transform infrared spectroscopy, X-ray diffraction and Raman spectroscopy. The electrochemical performance of the fabricated electrodes was investigated by cyclic voltammetry, galvanostatic charge–discharge and electrochemical impedance spectroscopy. Even treated with extremely low H2SO4 concentration and small KOH:hydrochar ratio, the maximum SBET of 1365 m2 g−1 for an AC was obtained after gamma irradiation. This was attributed to radiation-induced interconnected network formation generating micropores within the material structure. The supercapacitor electrodes exhibited electric double-layer capacitance giving the highest specific capacitance of 309 F g−1 as well as excellent cycle stability within 10,000 cycles. The promising results strongly ensure high possibility of the eco-friendly method application in supercapacitor material production.
Recently fossil energy becomes less attractive due to its limited long-term energy supply and environmental issues. On the other hand, alternative energy has been increasingly taken into consideration to ensure sustainability and clean environment. Regardless of energy sources, all renewable energy processing requires a stable and reliable energy storage system (ESS). Considerable attentions have been drawn to supercapacitors as they offer high stability, rapid charging ability and wide operating temperature. This class of energy storage devices also exhibits high power density with energy efficiency up to 98%1. Unlike traditional solid dielectric capacitors, the total capacitance of supercapacitors relies essentially on electric double-layer capacitance (EDLC) and electrochemical pseudocapacitance. In fact, the capacitance value of a supercapacitor is influenced by several factors, namely specific surface area, pore structure, electrical conductivity and surface functionality of the electrodes. EDLCs normally provide specific surface area greater than 500 m2 g−1 leading to much higher specific capacitance than those of conventional capacitors. Fast charge accumulation reversibility in EDLCs also allows completion of charge/discharge cycle within seconds2. As opposed to rechargeable batteries whose cyclic life is shorten after a number of chemical reaction-based charge/discharge processes, EDLCs can maintain exceptional electrode structure and high capacity even after millions of operating cycles3. Unfortunately EDLCs commercially available still suffer from a much lower energy density (< 10 Wh kg−1) when compared to those of batteries (35–40 Wh kg−1)4. In fact, the energy density and total capacitance of a supercapacitor can be improved when introducing an additional charge storage–charge transfer mechanism so-called pseudocapacitance to the electrode material. The mechanism takes place through fast and reversible oxidation–reduction reactions at the electrode/electrolyte interface and in the bulk electrode material. In other words, this faradaic process helps decrease the energy gap between EDLCs and batteries5,6. Pseudocapacitive behaviors in SCs are mainly governed by the presence of heteroatom-containing functional groups on the electrode surface. Metal oxides, metal nitrides and conducting polymers are the most widely used materials in pseudocapacitor electrodes. The production process however requires complex procedures in combination with a number of toxic substances, thus posing environmental risks5.
Recently biomass-derived activated carbons (ACs) are considered an attractive choice for electrode active materials as this group of porous materials can be produced from low-cost and renewable agricultural wastes. They have been synthesized from a wide variety of starting materials, including potato, acorn shells, pistachio shells, peanut shells, algarroba wood, macadamia nut shells, walnut shells, corncob, durian shell, rubber seed shell and palm petiole7,8,9,10,11,12,13,14,15. Among alternatives, palm petiole (PP), produced during harvesting process of oil palm (elaeis guineensis), is material of interest since PP is largely generated from oil palm plantations, which are grown in Africa, South America, and Southeast Asia covering approximately 20 million hectares. Especially in Thailand, around 10.5 million tons of palm petioles are generated yearly16. More importantly, it has been shown that PP, containing 42.7% cellulose, 34.0% hemicellulose and 22.9% lignin, had porous nature even before treating13. To improve the energy storage performance of the electrode material, even a naturally porous AC precursor like PP still needs further activations. Generally carbon activation can be classified into two categories: (1) chemical activation via a high-temperature treatment of the precursor mixed with activating agents such as H2SO4, KOH, ZnCl2, H2O, H3PO4 and NaOH, and (2) physical activation through pyrolysis at high temperatures under activating gas such as CO2, steam, or gas mixture10,12,17,18,19,20,21,22. For chemical activation, low-cost H2SO4 is known to be a proper activating agent when it is used during hydrothermal carbonization of a biomass. During hydrothermal carbonization, this acidic agent can initially break large lignocellulosic structures into smaller parts and further promote polymerization of the small molecules first produced even under mild conditions. This series of reactions will give sulfonated biochar as a product23. KOH is another well-proven activating reagent which is suitable for pyrolysis at high temperature. When mixed with an AC precursor and further pyrolyzed, KOH can react with the sample generating a number of gaseous products creating porosity throughout the structure. The resultant ACs normally show a high specific surface area with mesopores17,24. The pore sizes of the synthesized ACs are comparable to that of K+ ion; therefore, this is extremely beneficial when the prepared electrode used with KOH electrolyte. After an activation or a series of activations, the resultant materials known as ACs are expected to have higher specific surface area and porosity which can facilitate the supercapacitor behaviors. Besides, a subsequent modification by radiation processing such as gamma irradiation can be introduced. Radiation processing is one of promising methods for modification of carbon materials since the approach is environmentally friendly and it offers possible large-scale production with uniformity. When a medium is gamma irradiated, a number of highly reactive chemical species so-called radiolytic primary species are generated and this medium is said to undergo gamma radiolysis. For example, gamma radiolysis of water produces (e)−aq, ·OH, H2O2, H·, H2 and HO2/O2−25. Material modification by gamma radiolysis is based on the chemical reactions between the radiolytic primary species and the material surface. The studies on carbon cloth demonstrated that upon gamma irradiation, surface phenolic groups and acidity of the carbon material were clearly increased when treated in air26, and the number of oxygenated groups on the sample surface was reduced in an alkaline medium27. Another publication regarding surface chemistry modification of activated carbon by gamma radiation also showed that desirable surface functionality and significantly increased sp2 hybridization were found in the post-irradiated materials28. It is therefore strongly evident that gamma irradiation on carbon structures can improve quantity of oxygenated functional groups on the material surface as well as its sp2 hybridization both of which can aid in facilitating charge-storage and charge delivery in a carbon-based supercapacitor. In addition, application of radiation processing can help reduce the use of hash chemicals and energy during the activation processes.
In this work, we propose an environmentally friendly method for palm petiole-derived AC production based on chemical and physical activations in conjunction with radiation processing. In spite of various studies on AC preparation from PP, to the best of our knowledge, there is no publication on PP activated carbon preparation via low concentration H2SO4/KOH chemical and physical activations in combination with gamma irradiation specifically for the purpose of supercapacitor application. The novelty of this research is to produce ACs from abundantly local palm petiole via a new environmentally friendly three-step strategy consisted of H2SO4 hydrothermal carbonization at 160 °C, KOH-activating pyrolysis under Ar atmosphere at the target temperatures of 700 and 800 °C, and gamma radiation treatment at different doses under NaNO3 oxidizing environment. This is also the first study to clearly demonstrate that gamma irradiation can aid in increasing the specific surface area of a carbon material by inducing interconnected networks of the micropores within the structure. The textural and chemical properties of the prepared activated carbons were characterized using various techniques. The materials were finally applied as an active material for a supercapacitor electrode, and its electrochemical behaviors were tested according to CV, GCD and EIS measurements.
Palm petiole (PP), biomass from abundantly available palm oil tree in Tha Sala district, Nakhon Si Thammarat, Thailand, was used as carbon precursor. At first, the petiole was sliced into thin and small pieces and dried at 90 °C for 15 h. Then, it was ground into powder with a mixer mill and a ball mill, respectively. Only the powder particles with the size up to 250 µm were collected for further steps. All the experiments were thoroughly conducted using deionized water (DI water).The chemicals including 98% sulfuric acid (H2SO4, RCI Labscan), 85% potassium hydroxide (KOH, KemAus), 37% hydrochloric acid (HCl, QReC) and 99% sodium nitrate (NaNO3, Loba Chemie) were all analytical grade and used as received.
For step 1, hydrothermal carbonization, H2SO4 was used as a catalyst for hydrolysis and cleavage of the biomass. Initially, 10 g of the biomass powder was dispersed in 100 mL 0.6%wt H2SO4 aqueous solution and stirred for 30 min. The mixture was then transferred into a stainless steel reactor with Teflon liner and cured at 160 °C for 12 h. After cooling down to room temperature, the obtained brown product, called hydrochar, was washed several times with DI water until pH reached neutral, filtered, and dried at 80 °C for 8 h. This washing step was done to eliminate organic by-products and to adjust pH as the pH value during hydrothermal carbonization normally decreased due to the formation of organic acids. Before further activation, the collected product was characterized with FTIR. For step 2, subsequently the hydrochar was mixed homogeneously with KOH (impregnation ratio of 1:1) and carbonized and activated via pyrolysis in the horizontal furnace tube at 700 and 800 °C for 2 h with the ramp rate of 10 °C/min under Ar atmosphere (flow rate of 100 ml/min). KOH was used as activator at this step to increase porosity. The resultant black products, known as activated carbons (ACs), were later dispersed in 10% HCl solution for 1 h and washed several times with DI water to remove the leftover ash contents and K+ ions on the material surface until neutral pH was achieved. HCl washing method can reduce ash content down to the range of 0–9.4%29,30,31.The solid products were later filtered and dried at 80 °C for 8 h. The as-prepared ACs at 700 and 800 °C were denoted as PP700 and PP800, respectively.
For step 3, gamma irradiation, 2 g of each activated carbon was dispersed in a 0.1 M NaNO3 solution making the total volume of 50 ml, and purged with N2 for 20 min. After purging, the mixture was irradiated with gamma ray from a cobalt-60 irradiator (30366 Ci, dose rate of 4 kGy/h) at the Thailand Institute of Nuclear Technology. The irradiation periods were 6.25, 12.5 and 25 h for the total doses of 25, 50, and 100 kGy, respectively. Harwell Amber Perspex dosimeter was used for dosimetry. The obtained products were washed with deionized water, filtrated, and dried overnight at 80 °C. The irradiated activated carbons were denoted as PP700_25, PP700_50, PP700_100, PP800_25, PP800_50 and PP800_100 where the digits following low dash represented the gamma dose. Besides, the activated carbons without irradiation (controlled set) were also used for comparison, and denoted as PP700_0 and PP800_0.
Field emission scanning electron microscope–energy dispersive X-ray spectroscopy (FESEM–EDS) analysis was conducted to investigate the morphology and elemental composition of the materials (ZEISS, MERLIN Compact-Oxford, Aztec ED). The Brunauer–Emmett–Teller (BET) surface areas of the materials were obtained from ASAP2460 (at 300 °C degassing temperature). T-plot and density functional theory (DFT) methods were also applied for porosity analysis. The variation of functional groups of hydrochar and activated carbons was investigated using fourier transform infrared spectroscopy (FTIR, BRUKERS, Tensor 27) with a scan range of 4000–500 cm−1. The crystallinity and chemical states of the samples were determined by powder X-ray diffraction (XRD, PANalytical) with a Cu Kα radiation, λ = 1.54056 Å and Raman spectroscopy (XploRA PLUS Raman, HARIBA) at 532 nm.
To fabricate the supercapacitor electrode, 14 mg of activated carbon, 2.5 mg of a carbon black conductive additive, 10 µl of a polytetrafluoroethylene (PTFE) binder and 600 µl of ethanol were mixed. It should be noted that carbon black was used as a conductive additive since it has a better stacking structure compared to activated carbon, thus facilitating electron flow in the fabricated electrodes. The mixture was then sonicated for 30 min. The slurry was coated onto a graphite sheet with 1.5 cm × 2 cm active surface area. The loading mass of the active material was around 3–5 mg. The electrochemical tests were conducted using a potentiostat (Metrohm Autolab, PGSTAT302 N) with a three-electrode system in 1 M KOH electrolyte under ambient condition. Cyclic voltammetry (CV) curves were recorded at different scan rates (0.01–0.1 V/s) to investigate the electrochemical behaviors of the materials. Galvanostatic charge–discharge (GCD) was performed at varied current densities (1–10 A g−1) to study the charge–discharge nature of the prepared electrodes and to calculate the specific capacitance. Electrochemical impedance spectroscopy (EIS) in the frequency range of 100 kHz–0.1 Hz with 0.1 V was also recorded to detect the electrical response at the electrode interface.
In this study PP biomass was first hydro-thermalized with H2SO4 at 160 °C for 12 h. The hydrochar produced was later mixed homogeneously with KOH activating agent at the hydrochar:KOH ratio of 1:1. Subsequently the mixture was carbonized and activated through pyrolysis under Ar atmosphere at 700 and 800 °C for 2 h. The activated carbons obtained were then irradiated with gamma radiation in deaerated aqueous NaNO3 at the total doses of 25, 50 and 100 kGy. Subsequently, the post-irradiated products were characterized using FESEM-EDS, N2 adsorption/desorption isotherms with BET surface area analysis, FTIR, XRD and Raman spectroscopy. The porous carbons were finally used as supercapacitor electrode material and undergone electrochemical measurements including CV, GCD and EIS. The experimental scheme is described in Fig. 1. The yields of the activated carbons produced at 700 °C and 800 °C were 29.42 and 28.68%, respectively. The values were obtained from \(\frac{{{\text{AC }}\,{\text{mass}} \times { }100}}{{{\text{mass }}\,{\text{of }}\,{\text{starting}}\,{\text{ material}}}}\) .
In general, upon gamma irradiation water molecules are excited and ionized giving a number of highly reactive radicals and molecules called radiolytic primary species as shown in Reaction 1 (R1)32. The G-values, defined as the number of the species produced per 100 eV of energy absorbed, for (e−)aq, ·OH, H2O2, H·, H2, and HO2/O2− are 2.70, 2.87, 0.61, 0.61, 0.43 and 0.026, respectively25. In the presence of NaNO3, the hydrated electrons (e−(aq)) and ·H produced react with NO3- ions as described in Reaction 2 (R2) with the rate constant of 9.7 × 109 M-1 s-1 and Reaction 3 (R3) with the rate constant of 1.0 × 107 M−1 s−1, respectively33,34,35. R2 and R3 lead to e-(aq) and ·H scavenging which also reduce the chain reactions generating H236. As a result, the key radiolytic primary species remain in the medium are ·OH and H2O2, and the overall chemistry system is converted into a fully oxidizing condition. In a presence of activated carbon the remaining oxidizing species can therefore react with the surface functional groups leading to surface modification of the carbon materials.
FESEM images together with EDS analysis results, shown in Fig. 2, revealed the highly porous structure of the prepared materials with chemical composition containing around 89.0% carbon, 10% oxygen and 1% of silicon that may have contaminated from the cultivating environment (Fig. 2i). It should be emphasized that light elements such as hydrogen cannot be detected by the EDS elemental analysis. In addition, Au signals were observed in the EDS spectrum since gold was used in the conductive coating procedure for the detection. According to Fig. 2, the un-irradiated materials, PP700_0 (Fig. 2a) and PP800_0 (Fig. 2e) showed a porous structure with holes and cracks. As the material received gamma radiation at the total dose of 25 kGy, unnoticeable effect was seen in the case of PP700_25 (Fig. 2b). However, in the case of PP800_25 (Fig. 2f), it was clearly observed that some of the wall were broken forming interconnected networks of porous structures. These results may indicate that the consequent radiation effect can be governed dramatically by the activating temperature. When the total dose increased from 25 to 100 kGy, the interconnection between the holes obviously increased in both 700 and 800 °C sets (Figs. 2c,d,g,h). It is worth noting that at the maximum radiation dose of 100 kGy in the case of 700 °C, formation of small holes was noticed in addition. This was the evidence showing that small holes were created by bombardment of the carbon surface with the radiolytic oxidizing species before interconnecting of the small holes to form the networks. These highly porous structures are beneficial for supercapacitor performance as an increase in specific surface area can assist ions accessibility, charge storage and charge transfer in the active AC electrodes8,37.
FESEM images of the synthesized ACs at 10.00 kV: (a) PP700_0 (b) PP700_25, (c) PP700_50, (d) PP700_100, (e) PP800_0 (f) PP800_25 (g) PP800_50 and (h) PP800_100, and (i) EDS spectrum of PP800_0.
More details about porosity were investigated by N2 adsorption/desorption isotherms with BET surface area analysis, t-plot and density functional theory (DFT) methods. From the N2 adsorption/desorption isotherms shown in Fig. 3a,b, the synthesized materials were classified as Type I and Type IV isotherms with Type H4 hysteresis according to IUPAC criteria38,39. For Type I, a steep N2 uptake was observed at low relative pressure (P/P0) indicating the presence of adsorbent-adsorptive interactions in very narrow pores (supermicropores, 0.7–2 nm) in the materials40. For Type IV, capillary condensation was accompanied by Type H4 hysteresis, revealing a mesopore characteristic. The data obtained therefor suggested the coexistence of micropores and mesopores in the graphitic carbons. The adsorbed quantities of the materials in the PP800 series were significantly higher than those in the PP700 series implying higher specific surface areas. The calculated porosity parameters: specific surface area, pore volume and average pore size are shown in Table 1. The total pore and micropore volumes were calculated by the t-plot method. The specific surface areas of the PP700 series lied between 770 and 996 m2 g−1 which were apparently lower than those in the PP800 series in the range of 1275–1365 m2 g-1. In both PP700 and PP800 series, after gamma irradiation the specific surface areas were clearly increased with the highest values of 996 m2 g−1 for the PP700 series (25 kGy) and 1365 m2 g−1 for the PP800 series (50 kGy). The pore sizes of the materials were found to fall in the micropore region with the average size around 1.6–1.7 nm. The pore size distribution, calculated using MicroActive for ASAP 2460 Version 2.01 from Micromeritics based on DFT model with a non-negative regularization method, can be seen in Fig. 3c. It is crystal clear that gamma irradiation with a relatively low radiation dose helps increase the specific surface area of the materials. In general, radiation processing can be used to improve material properties such as functional groups and porosity, and the quality of the desired properties normally increases with radiation dose before radiation damage occurs. In other words, at a lower radiation dose, a number of reactive species react with the material surface causing bond breaking and functional group alteration, and as a consequence, small pores are generated. At a high radiation dose, however a number of pores with larger dimensions are formed, resulting in the reduction of specific surface area. Saha et al. demonstrated that porosity of poly-[ethylene oxide] (PEO) powder was increased at gamma irradiation dose up to 3 kGy, and the porosity was decreased linearly when the dose was raised higher from 3 to 30 kGy41. This similar trend of radiation effect on materials was also reported previously by other research groups42,43,44. Therefore, the appropriate total dose used for a specific purpose of material development or improvement needs to be explored.
(a) N2 adsorption/desorption isotherms of PP700 series, (b) N2 adsorption/desorption isotherms of PP800 series and (c) pore size distribution of the synthesized ACs based on DFT model with Non-negative Regularization method.
As it is known that hetero-atom containing functional groups on the material surface play an important role in its electrochemical properties. Especially in a pseudocapacitive electrode material, these functional groups help facilitate charge storage and charge transfer through rapid and reversible redox reactions at the electrode/electrolyte interface45,46,47. The surface functionalities of the materials were, therefore, investigated using FTIR. The results are shown in Fig. 4. As seen in Fig. 4, the hydrochar sample exhibited a broad peak around wavenumber 3340 cm−1 which belonged to OH stretching of carboxylic acid, alcohol and phenol. The peaks with small intensities at 2920 cm−1 and 2850 cm−1 were assigned to C–H stretching of methyl group and H–C=O stretching of aldehyde, respectively. Weak absorptions at 1700 cm−1 and 1600 cm−1 were due to vibrations of C=O band of aliphatic ketone/carboxylic acid and aromatic C=C48. The peaks around 1110 cm−1 and 1030 cm−1 were attributed to C–O stretching of ether and R–OH of primary alcohol. Therefore, the possible oxygen-containing groups in the hydrochar produced by H2SO4 hydrothermal carbonization were carboxylic acid, alcohol, phenol, aldehyde and ether. When biomass is hydro-thermalized, its structure is rearranged through reactions with water molecules. In a presence of an acid, the process is catalyzed leading to a faster decomposition of the bio-macromolecules49. The hydrochar formed by this technique was proven to have high surface area50 which in turn could well serve as a pre-treated material for activated carbon production. For the resultant ACs, the obtained spectra were similar to the hydrochar spectrum. However, the peak intensity of C–H around 2920 cm−1 clearly decreased and the C=O peak at 1700 cm−1 was unnoticeable after conversion into ACs. This was owing to evaporation of volatile species at high temperature during pyrolysis. The peak of C-O stretching around 2350 cm-1 was also observed in some samples. This may be due to contamination of CO2 during the measurement. The un-irradiated and irradiated ACs showed almost the same main functional groups. According to the FTIR spectra, the AC surface structures consisted of OH stretching (3420 cm−1), C–O stretching (2350 cm−1), CH stretching (2330 cm−1), C=C stretching (1580 cm−1), and C–O stretching (1110 cm−1) peaks which could be assigned to alcohol, phenol, carboxylic acid, aromatic ring and alkene. The peak assignments are summarized in Table 251.
FTIR spectra of the hydrochar and synthesized ACs.
The crystallinity of the materials was studied using powder X-ray diffraction (XRD). The XRD patterns of the synthesized ACs are shown in Fig. 5. All samples exhibited two broad peaks, one in the range of 17–23° and another around 43° which were corresponding to 002 and 100 diffraction planes, respectively. These results revealed the amorphous and turbostratic structure of the porous materials that was microcrystalline with randomly orientation. The lower shift of 002 plane from 26° in pure graphite52 to 17–23° indicated the defective nature of the materials with a presence of a short range order of the graphene layers. For the un-irradiated ACs (PP700_0 and PP800_0), the diffraction peaks for 002 plane centered around 2-theta 23°. The peak, however, shifted to 20° in PP700_25, PP700_50, PP700_100 and PP800_25. In PP800_50 and PP800_100, the 002-plane peaks even lower shifted to 17°. This clearly suggests that the activation (pyrolysis) temperature and radiation dose play a significant role on the interlayer distance of the graphitic structure. Moreover, in both series the peak broadening in the XRD patterns of the samples was found to decrease after the materials were irradiated at all doses. As peak broadening indicates low level of crystallinity in the materials, therefore it can be mentioned that gamma irradiation at appropriate dose helps improve structural order in the carbon samples. With excess radiation energy, enormous structural changes may occur causing a decrease in the level of crystallinity. Although high pyrolysis temperature and high radiation dose may lead to low crystallographic order in a carbon material, its capacitive property may still remain with the compensating porosity.
XRD patterns (Cu Kα radiation, λ = 1.54056 Å) of the synthesized ACs.
As it has been intensively demonstrated that degree of graphitization in carbon materials can effectively facilitate the charge and electrolytic ion transfer in supercapacitor application53,54,55,56, Raman spectroscopy was carried out to further study the graphitization degree of the prepared materials. The obtained results are shown in Fig. 6. The Raman spectra contained two board peaks around 1330 cm−1 (D band) which was associated to A1g breathing mode of disordered sp3 carbon, and around 1580 cm−1 (G band) corresponding to E2g in-plane vibration of sp2 carbon of conjugated chains and aromatic rings in graphitic layer57. It is well-established that the graphitization degree of the materials can be determined by the intensity ratio of D band over G band (ID/IG) based on Tuinstra and Koenig law, and the lower ratio value represents the higher degree of graphitization58,59,60. The values calculated for all samples as shown in Fig. 6 were in the range of 0.91–0.99, revealing amorphous nature of the materials with strong graphitization. The lowest ID-to-IG ratios of both series, referring to the highest degree of graphitization or the highest ordered nature, were given by PP700_25 and PP800_50 with the values of 0.91 and 0.92, respectively. The high graphitization degree of PP700_25 was in good agreement with the XRD results indicating enhancement of ordered graphitic layers in the carbon material after irradiation. However, when the radiation dose was raised further to 50 and 100 kGy, interconnection between the micropores increased resulting in more disordered structures with lower graphitic degrees. For PP800 series, given 25 kGy of radiation, this level of radiation was sufficient to perturb the carbon structure thus increasing the number of sp3 carbons, but not enough to enhance the sp2 hybridization in the material. As the radiation energy was increased to 50 kGy, the perturbation was enough to change the sp3 units into sp2 domains. With higher radiation dose at 100 kGy, however, excess radiation caused more wall breakings similar to the PP700 cases and lowered the graphitization degree. Improvement of graphitization degree (sp2 hybridization) directly enhances the electrical conductivity of the material, hence supporting its capacitive characteristic.
Raman spectra of the ACs obtained at laser wavelength 532 nm.
To get an insight into the electrochemical behaviors of the materials, supercapacitor electrodes were fabricated from the synthesized ACs and electrochemically tested in 1 M KOH electrolyte using a standard three-electrode system with Pt wire and Ag/AgCl as counter and reference electrodes, respectively. Cyclic voltammetry (CV) was used to detect the electrochemical behaviors of all prepared electrodes. The CV profiles at different scan rates (0.01–0.10 V s−1) in − 0.20 to 0.20 V potential windows of selected ACs from PP700 (PP700_25) and PP800 (PP800_50) series are demonstrated in Fig. 7a,b, respectively. According to Fig. 7, the voltammogram of each sample at a high scan rate revealed a near-perfect rectangular shape which was predominantly characteristic of EDLC. It was also found that the shapes of the current response remained unchanged when the scan rate increased from 0.02 to 0.10 V s−1. This suggests strong electrochemical reversibility that is a low barrier for electron transfer at the electrode/electrolyte interface61. This EDLC characteristic was attributed to the mesoporous nature of the carbonaceous materials which helped support the formation of the electric double layer62. Surprisingly at high scan rates pseudocapacitance behaviors of the samples, which was normally indicated by the presence of a redox peak at high potential, ascribed to the oxygenated functionalities on their surface was not detected. However, it was found that the curve recorded at the lowest scan rate (0.01 V/s) exhibited the least rectangular behavior. There are two possible explanations for this phenomenon. The first explanation is related to ion saturation at low scan rate. For an EDLC, initially, when the potential is increased, the ion concentration increases rapidly leading to increasing in current density. However, when ion concentration at the electrode surface reaches its maximum value, the electrode surface accumulation of ion gets slower, the current density decreases showing a CV curve with a hump63. The second explanation is related to the presence of redox reactions. The humps characteristic of redox reactions was attributed to the content of oxygenated surface functional groups as supported by the FTIR spectra. However, the recorded curve was asymmetric showing a broad reduction peak without a corresponding oxidation peak of equal magnitude, thus indicating some resistance. The similar results to our CV shapes at the lowest scan rate implying pseudocapacitive behavior were reported previously64,65,66,67. The explanation for this is that the Faradaic process can occur on both surface and interior of the electrode68, and such process is considered slow when compared to non-Faradic, such as EDLC. Therefore, it is possible that with a slow scan rate, more time allows redox reactions to occur at the interface and on the interior causing the deviation of the CV curve. On the other hand, at higher scan rates less time for redox reactions to occur; thus, the surface process dominates the energy storage mechanism, and the CV curves exhibit the ideal EDLC behavior. The influence of surface and bulk processes on CV scan rate for pseudocapacitive electrodes was studied earlier69. In this study, it was concluded that at a low CV scan rate, the mechanism was taken over by the bulk process. Therefore, the possible explanation for more deviation at the lowest scan rate could be related to ion saturation at the electron surface or redox mechanism. However, it is more likely that the deviation of the CV curve at the lowest scan rate was due to the presence of Faradaic process as supported by the FTIR and GCD results (discussed in the following paragraph). The mechanism of charge storage in the materials was, thus, a combination of EDLC and pseudocapacitance. The percentage of the capacitive contribution from each storage mechanism is particularly important. The study of EDLC and pseudocapacitance contribution under varied preparation conditions could be another research topic on its own, and we suggest this as future study. The voltammograms for all prepared AC electrodes are demonstrated in Fig. 7c.
CV profiles obtained from a three-electrode system with Pt wire counter electrode and Ag/AgCl reference electrode in the potential window from − 0.2 to 0.2 V: (a) PP700_25 at varied scan rates, (b) PP800_50 at varied scan rates and (c) all synthesized ACs at 0.1 V s−1.
Since it directly describes capacitive behavior, the current density is a crucial factor for supercapacitors. The capacitive behavior of the AC-derived supercapacitor electrodes was further investigated using galvanostatic charge–discharge (GCD) technique. The GCD curves from PP700_25 and PP800_50 at different current densities were illustrated in Fig. 8a,b, respectively. Similar results were obtained from both materials showing a deviation from a typical triangular shape at low current densities due to asymmetric charge and discharge durations. At lower current densities, the materials exhibit lower Coulombic efficiency which is defined as \(\frac{discharging\, time}{{charging\, time}} \times 100\%\) . In other words, the electrodes give high Coulombic efficiency at high current density reflecting their great storage ability which is a desirable feature of a supercapacitor material70. Furthermore, the deviations from symmetry in the GCD curves were due to the presence of the Faradaic charge transfer in additional to the EDLC mechanism. The Faradaic processes were possible with the presence of oxygen-containing surface functional groups indicated by the FTIR spectra and CV curves at the lowest scan rate.
(a) GCD curves of PP700_25 at current densities 1–10 A g−1, (b) GCD curves of PP800_50 at current densities 1–10 A g−1, (c) GCD curves of all synthesized ACs at current density 1 A g−1, (d) specific capacitance (Cp) from all ACs plotted against gamma dose, (e) capacitance retention (%) obtained from the PP800_50 electrode (inset depicts some of the initial and final charge discharge cycles), (f) GCD curves before (1st cycle) and after (10,000 cycles) cycling and (g) Nyquist plot of PP700_25 and PP800_50 electrodes measured in the frequency range of 10 kHz–0.1 Hz fit with the equivalent circuit.
Moreover, as it is well-established that specific surface area is the key factor governing the specific capacitance (Cp) of a supercapacitor electrode, given the relatively high specific surface areas (767–1365 m2 g-1) discussed earlier, the prepared graphitic carbons were expected to provide high Cp values. The GCD profiles of all electrodes at current density 1 A g−1 were recorded (Fig. 8c) and used for Cp calculation according to Expression 1 (E1)71,
where Cp is the specific capacitance (F g−1), Im is the current density (A g−1), derived from \({I}_{m}=\frac{\mathrm{discharge current }(\mathrm{A})}{\mathrm{active mass on the electrode surface}}\) , ΔV is the applied potential window and Δt is the discharging time. The specific capacitance and discharge time for the ACs were shown here as well at doses of 25, 50, and 100, and the controlled sample does not differ much. As the gamma-ray dose is increased, the discharge time and capacitive capacity of the electrodes first increase and then decrease, which can also be attributed to the increase in active surface area and graphitization degree that is a result of radiation at different doses. The PP700 (PP700_25) and PP800 (PP800_50) series samples were found to have the longest discharge times. This finding is in line with the EIS and CV findings that the ideal dose can improve electrode performance, indicating that the use of inadequate and excessive dosage levels must be avoided while producing electrodes72. All electrodes showed a sharp reduction in the initial voltage of the discharge curve in Fig. 8c, and this dip was caused by the electrolyte ions' diffusion-limited mobility within the electrode pores. The ESR (equivalent series resistance) of the supercapacitor cells is related to this restriction73. The calculated Cp values plotted against gamma radiation dose are shown in Fig. 8d. The values obtained are in the range of 224–309 F g−1. It was found that upon irradiation the Cp increased and after reaching the maximum value the number gradually decreased with radiation dose. These results could be well explained by the fact that irradiation at an appropriate dose led to enhancement of specific surface area, crystallinity and graphitization level in the carbonaceous structure; however, when the radiation dose was raised beyond this point, radiation damage occurred causing the decrease in all parameters, which were clearly proven by the results from FESEM, BET surface area analysis, XRD and Raman spectroscopy. The highest Cp values of each series were given by PP700_25 and PP800_50 with the values of 277 and 309 F g−1, respectively. Both samples with the highest Cp exhibited the highest specific surface area and graphitization degree within the series. Specific surface area is one of the most important parameters of a supercapacitor electrode as a high specific surface area can provide more adsorption sites for the charges and facilitate mass/charge transfer at the electrode/electrolyte interface. In turn, the amount of energy stored in the device is directly proportional to the specific surface area based on the Helmholtz model74. In addition to the specific surface area, the degree of graphitization is the primary factor supporting electrical conductivity in the material, thus improving charge transfer in the system as well. Unfortunately the two factors normally have a negative correlation, i.e., in order to have a high specific surface area or porosity, the material needs to sacrifice its structural order or graphitization degree53,75,76. In the case of PP700_25 and PP800_50, the materials possessed high surface area and simultaneously retained great graphitization, hence having an excellent charge storage-charge transfer balance which ultimately resulted in the high Cp values. This is clear evidence proving that our preparation method is a promising choice for AC production with high surface area and high graphitization degree. More importantly, the Cp values obtained are considered high when compared with those reported in the literature. Table 3 shows the comparison of the Cp values from this work and those previously published based on similar chemical and physical activation methods with electrochemical measurements in a three-electrode setup. The electrode materials in all studies were biomass-derived activated carbons. The capacitance value of 309 F g−1 (from 1 M KOH electrolyte system) is comparable to the reported values, and it is considered relatively high. According to Table 3, 309 F g−1 is higher than the values from all similar studies with 1 M KOH electrolyte. This value is even higher than most of the specific capacitances obtained from a 6 M KOH electrolyte system. When a higher concentration of KOH electrolyte applied (in this case 6 times higher), the ions participating in the redox mechanism are increased; therefore, a higher specific capacitance should be expected, especially if the energy storage mechanism gets involved with pseudocapacitance. According to the comparison, it is obvious that a combination of chemical-physical activation and gamma irradiation in this work can be an effective method of AC synthesis for a high-performance supercapacitor electrode.
A stability test with PP800_50 was conducted up to 10,000 cycles in a potential window of − 0.2 to 0.2 V. To obtain the capacitance retention, the Cp value at 1 A g−1 current density was calculated for every 500 cycles and compared with the first-cycle value. The results obtained are illustrated in Fig. 8e. In the first 4000 cycles, the specific capacitance (Cp) was found to decrease to 92.6% of the initial value. This may be attributed to less migration of the ions through the porous structure. However, after 4500 cycles the value gradually increased and reached 100.4% at cycle 5500 indicating rearrangement of the electrode surface structure with more cycling numbers to promote faster ion migration. The capacitance retention slowly decreased and finally stabilized around 91.3–94.0% within 10,000 cycles ensuring the great endurance of the prepared AC-based electrode. Comparison between the GCD curves before (first cycle) and after (10,000 cycles) cycling can be seen in Fig. 8f, showing only little change in the energy storage performance.
The charge transportation ability at the electrode/electrolyte interface was studied using electrochemical impedance spectroscopy (EIS) at the bias potential of 0.1 V in the frequency range of 100 kHz–0.1 Hz. The results from PP700_25 and PP800_50 giving the highest specific capacitance values in each series are described in the form of Nyquist plots (Fig. 8g). According to Fig. 8g, the Nyquist plots are composed of two segments: a semicircle part in the high-frequency region and an inclined line in the low-frequency region. The semicircle part demonstrates the combination of electrolyte resistance and charge transfer resistance, whereas the linear segment represents the ionic diffusion process. Fitting the Nyquist plots using NOVA 1.11 software gave the equivalent circuit illustrated in Fig. 8g. According to the equivalent circuit, Rs is the uncompensated (internal) resistance of the cell, Rp is referred to the charge transfer resistance, CPE is the Constant Phase Element and W is the Warburg impedance showing the ionic diffusion through the diffusion zone. The Rs values obtained for PP700_25 and PP800_50 electrodes were 1.8 and 2.0 Ω, respectively. The Rs value was lower for the PP700_25, which suggests that introducing low amount of Gamma dose at 700 °C reduces the internal resistance of the electrodes. The values of Rp for both electrodes were around 70 mΩ. Considering the particularly small Rp values, the fabricated electrodes are suitable for supercapacitor application.
In this study, activated carbons (ACs) were successfully synthesized from palm petiole using a three-step strategy composed of H2SO4 hydrothermal carbonization, KOH-activating pyrolysis and gamma radiolysis under oxidizing condition. The prepared graphitic carbons were highly microporous with porosity greatly influenced by activation temperature and gamma dose. Given higher activation temperature, a larger specific surface area was clearly developed. Gamma-induced modification of the carbon surface structure resulted from the bombardment of the carbon surface with radiolytic oxidizing species creating interconnection between the micropores. The appropriate radiation dose needed to be explored as excess radiation energy caused larger pores leading to low specific surface area. The maximum specific surface area of 1365 m2 g−1 was given by the AC pyrolized at 800 °C with 50 kGy of gamma dose (PP800_50). The surface functional groups of the porous carbons could be assigned to alkene, aromatic ring, alcohol, phenol and carboxylic acid. The level of crystallinity was increased after irradiation with pronounced (002) and (100) planes. The activation temperature and radiation dose played a significant role on the range order and the interlayer distance of the graphitic structure. Excess radiation caused more wall breakings, thus lowering the graphitization degree. When an optimized radiation dose was applied, however, high surface area and great graphitization (high conductivity) can be both obtained. The produced supercapacitor electrodes showed outstanding electrochemical properties with a dominant EDLC mechanism. The specific capacitance of PP-AC electrodes was apparently dictated by the specific surface area. The PP800_50 electrode was found to be the most suitable for supercapacitor application. It showed the highest specific capacitance of 309 F g−1 and exhibited small total internal resistance and polarization resistance around 2.0 and 70 mΩ, respectively, with excellent endurance up to 10,000 charge–discharge cycles. Therefore, the present research successfully demonstrated an efficient and environmentally friendly approach of biomass-derived activated carbon synthesis for supercapacitor electrode application.
The data that support the findings of this study are available from the corresponding author upon reasonable request.
Chatzivasileiadi, A., Ampatzi, E. & Knight, I. Characteristics of electrical energy storage technologies and their applications in buildings. Renew. Sustain. Energy Rev. 25, 814–830. https://doi.org/10.1016/j.rser.2013.05.023 (2013).
Article CAS Google Scholar
Yassine, M. & Fabris, D. Performance of commercially available supercapacitors. Energies https://doi.org/10.3390/en10091340 (2017).
Article Google Scholar
Fernando, J. 7 - Electrical double-layer capacitors. In Energy Storage Devices for Renewable Energy-Based Systems 2nd edn (eds Kularatna, N. & Gunawardane, K.) 199–237 (Academic Press, 2021).
Chapter Google Scholar
Obreja, V. V. N. Supercapacitors specialities - Materials review. AIP Conf. Proc. 1597(1), 98–120. https://doi.org/10.1063/1.4878482 (2014).
Article ADS CAS Google Scholar
Yi, C.-Q., Zou, J.-P., Yang, H.-Z. & Leng, X. Recent advances in pseudocapacitor electrode materials: Transition metal oxides and nitrides. Trans. Nonferrous Met. Soc. China 28(10), 1980–2001. https://doi.org/10.1016/S1003-6326(18)64843-5 (2018).
Article CAS Google Scholar
Okashy, S., Noked, M., Zimrin, T. & Aurbach, D. The study of activated carbon/CNT/MoO3 electrodes for aqueous pseudo-capacitors. J. Electrochem. Soc. 160(9), A1489–A1496. https://doi.org/10.1149/2.084309jes (2013).
Article CAS Google Scholar
Saka, C. "BET, TG–DTG, FT-IR, SEM, iodine number analysis and preparation of activated carbon from acorn shell by chemical activation with ZnCl2. J. Anal. Appl. Pyrolysis 95, 21–24. https://doi.org/10.1016/j.jaap.2011.12.020 (2012).
Article CAS Google Scholar
Zhan, Y. et al. Preparation of highly porous activated carbons from peanut shells as low-cost electrode materials for supercapacitors. J. Energy Storage 34, 102180. https://doi.org/10.1016/j.est.2020.102180 (2021).
Article Google Scholar
Şahin, Ö., Yardim, Y., Baytar, O. & Saka, C. Enhanced electrochemical double-layer capacitive performance with CO2 plasma treatment on activated carbon prepared from pyrolysis of pistachio shells. Int. J. Hydrogen Energy 45(15), 8843–8852. https://doi.org/10.1016/j.ijhydene.2020.01.128 (2020).
Article CAS Google Scholar
Matos, J., Nahas, C., Rojas, L. & Rosales, M. Synthesis and characterization of activated carbon from sawdust of Algarroba wood. 1. Physical activation and pyrolysis. J. Hazar. Mater. 196, 360–369. https://doi.org/10.1016/j.jhazmat.2011.09.046 (2011).
Article CAS Google Scholar
Saka, C., Baytar, O., Yardim, Y. & Şahin, Ö. Improvement of electrochemical double-layer capacitance by fast and clean oxygen plasma treatment on activated carbon as the electrode material from walnut shells. Biomass Bioenergy 143, 105848. https://doi.org/10.1016/j.biombioe.2020.105848 (2020).
Article CAS Google Scholar
Martins, A. C. et al. Removal of tetracycline by NaOH-activated carbon produced from macadamia nut shells: Kinetic and equilibrium studies. Chem. Eng. J. 260, 291–299. https://doi.org/10.1016/j.cej.2014.09.017 (2015).
Article CAS Google Scholar
Kanjana, K., Harding, P., Kwamman, T., Kingkam, W. & Chutimasakul, T. Biomass-derived activated carbons with extremely narrow pore size distribution via eco-friendly synthesis for supercapacitor application. Biomass Bioenergy 153, 106206. https://doi.org/10.1016/j.biombioe.2021.106206 (2021).
Article CAS Google Scholar
Ma, G. et al. Nitrogen-doped porous carbon derived from biomass waste for high-performance supercapacitor. Bioresour. Technol. 197, 137–142. https://doi.org/10.1016/j.biortech.2015.07.100 (2015).
Article CAS PubMed Google Scholar
Qu, W.-H., Xu, Y.-Y., Lu, A.-H., Zhang, X.-Q. & Li, W.-C. Converting biowaste corncob residue into high value added porous carbon for supercapacitor electrodes. Bioresour. Technol. 189, 285–291. https://doi.org/10.1016/j.biortech.2015.04.005 (2015).
Article CAS PubMed Google Scholar
Biomass Database Potential in Thailand [Online] Available: http://weben.dede.go.th/webmax/content/biomass-database-potential-thailand
Rajasekaran, S. J. & Raghavan, V. Facile synthesis of activated carbon derived from Eucalyptus globulus seed as efficient electrode material for supercapacitors. Diam. Related Mater. 109, 108038. https://doi.org/10.1016/j.diamond.2020.108038 (2020).
Article ADS CAS Google Scholar
Sun, K. & Jiang, J. C. Preparation and characterization of activated carbon from rubber-seed shell by physical activation with steam. Biomass Bioenergy 34(4), 539–544. https://doi.org/10.1016/j.biombioe.2009.12.020 (2010).
Article CAS Google Scholar
Williams, P. T. & Reed, A. R. Development of activated carbon pore structure via physical and chemical activation of biomass fibre waste. Biomass Bioenergy 30(2), 144–152. https://doi.org/10.1016/j.biombioe.2005.11.006 (2006).
Article CAS Google Scholar
Mestre, A. S., Hesse, F., Freire, C., Ania, C. O. & Carvalho, A. P. Chemically activated high grade nanoporous carbons from low density renewable biomass (Agave sisalana) for the removal of pharmaceuticals. J. Colloid Interface Sci. 536, 681–693. https://doi.org/10.1016/j.jcis.2018.10.081 (2019).
Article ADS CAS PubMed Google Scholar
Prauchner, M. J., Sapag, K. & Rodríguez-Reinoso, F. Tailoring biomass-based activated carbon for CH4 storage by combining chemical activation with H3PO4 or ZnCl2 and physical activation with CO2. Carbon 110, 138–147. https://doi.org/10.1016/j.carbon.2016.08.092 (2016).
Article CAS Google Scholar
Jain, A. et al. Mesoporous activated carbons with enhanced porosity by optimal hydrothermal pre-treatment of biomass for supercapacitor applications. Microporous Mesoporous Mater. 218, 55–61. https://doi.org/10.1016/j.micromeso.2015.06.041 (2015).
Article CAS Google Scholar
Zhou, Z. et al. Sustainable production of value-added sulfonated biochar by sulfuric acid carbonization reduction of rice husks. Environ. Technol. Innov. 24, 102025. https://doi.org/10.1016/j.eti.2021.102025 (2021).
Article CAS Google Scholar
Li, Q. et al. Preparation of biomass-derived porous carbons by a facile method and application to CO2 adsorption. J. Taiwan Inst. Chem. Eng. 116, 128–136. https://doi.org/10.1016/j.jtice.2020.11.001 (2020).
Article CAS Google Scholar
Morawetz, H. Radiation chemistry-principles and applications, Farhataziz and Michael A. J. Rodgers, Eds. VCH, New York and Germany, 1987, 641 pp. Price:. J. Poly. Sci. Part C Polym. Lett. 25(12), 510–510. https://doi.org/10.1002/pol.1987.140251209 (1987).
Article Google Scholar
Sekulić, DR, Babić, BM, Kljajević, LM, Stašić, JM & Kaluđerović, BV The effect of gamma radiation on the properties of activated carbon cloth.J. Serb.Chem.Soc.74(10), 8 (2009).
Article Google Scholar
Gao, S. et al. Improved energy storage performance based on gamma-ray irradiated activated carbon cloth. Electrochim. Acta 191, 908–915. https://doi.org/10.1016/j.electacta.2016.01.151 (2016).
Article CAS Google Scholar
Vega, E., Sánchez-Polo, M., Gonzalez-Olmos, R. & Martin, M. J. Adsorption of odorous sulfur compounds onto activated carbons modified by gamma irradiation. J. Coll. Interface Sci. 457, 78–85. https://doi.org/10.1016/j.jcis.2015.06.037 (2015).
Article ADS CAS Google Scholar
Yuliusman, N., Afdhol, M. K., Amiliana, R. A. & Hanafi, A. Preparation of activated carbon from palm shells using KOH and ZnCl2 as the activating agent. IOP Conf. Ser. Earth Environ. Sci. 75(1), 012009. https://doi.org/10.1088/1755-1315/75/1/012009 (2017).
Article Google Scholar
Zhang, Y. et al. Production of activated carbons from four wastes via one-step activation and their applications in Pb2+ adsorption: Insight of ash content. Chemosphere 245, 125587. https://doi.org/10.1016/j.chemosphere.2019.125587 (2020).
Article ADS CAS PubMed Google Scholar
Oglou, R. C., Gokce, Y., Yagmur, E., Ghobadi, T. G. U. & Aktas, Z. Highly stable Megalopolis lignite based N and S self-doped hierarchically porous activated carbons for high performance supercapacitors and ash content effects on performance. J. Energy Storage 46, 103817. https://doi.org/10.1016/j.est.2021.103817 (2022).
Article Google Scholar
Spinks, J. W. T. & Woods, R. J. An Introduction to Radiation Chemistry (Wiley, 1990).
Chen, R., Avotinsh, Y. & Freeman, G. R. Solvent effects on the reactivity of solvated electrons with ions in isobutanol/water mixed solvents. Can. J. Chem. 72(4), 1083–1093. https://doi.org/10.1139/v94-137 (1994).
Article CAS Google Scholar
Buxton, G. V., Greenstock, C. L., Helman, W. P. & Ross, A. B. Critical review of rate constants for reactions of hydrated electrons, hydrogen atoms and hydroxyl radicals (⋅ OH/⋅ O− in Aqueous Solution. J. Phys. Chem. Ref. Data 17(2), 513–886. https://doi.org/10.1063/1.555805 (1988).
Article ADS CAS Google Scholar
Loegager, T. & Sehested, K. Formation and decay of peroxynitrous acid: a pulse radiolysis study. J. Phys. Chem. 97(25), 6664–6669. https://doi.org/10.1021/j100127a016 (1993).
Article CAS Google Scholar
Patil, S. F., Bedekar, A. G. & Patil, R. M. γ-Radiolysis of isobutanol and nitrate in aqueous solution. J. Radioanal. Nucl. Chem. 158(1), 107–114. https://doi.org/10.1007/BF02034777 (1992).
Article CAS Google Scholar
Xia, K., Gao, Q., Jiang, J. & Hu, J. Hierarchical porous carbons with controlled micropores and mesopores for supercapacitor electrode materials. Carbon 46(13), 1718–1726. https://doi.org/10.1016/j.carbon.2008.07.018 (2008).
Article CAS Google Scholar
Thommes, M. et al. Physisorption of gases, with special reference to the evaluation of surface area and pore size distribution (IUPAC Technical Report). Pure Appl. Chem. 87(9–10), 1051–1069. https://doi.org/10.1515/pac-2014-1117 (2015).
Article CAS Google Scholar
Y. Nishi and M. Inagaki, "Chapter 11 - Gas Adsorption/Desorption Isotherm for Pore Structure Characterization," in Materials Science and Engineering of Carbon, M. Inagaki and F. Kang Eds.: Butterworth-Heinemann, 2016, pp. 227–247.
Sotomayor, F. J., Cychosz, K. A. & Thommes, M. Characterization of Micro/Mesoporous Materials by Physisorption: Concepts and Case Studies. Acc. Mater. Surf. Res. 3(2), 17 (2018).
Saha, M. Impact of gamma irradiation on porosity and pore distribution of poly [ethylene-oxide] films: Correlation with dielectric and microstructural properties. Indian J. Phys. 92, 12. https://doi.org/10.1007/s12648-017-1110-3 (2017).
Article CAS Google Scholar
Adhamash, E., Pathak, R., Qiao, Q., Zhou, Y. & McTaggart, R. Gamma-radiated biochar carbon for improved supercapacitor performance. RSC Adv. 10(50), 29910–29917. https://doi.org/10.1039/D0RA05764A (2020).
Article ADS CAS PubMed PubMed Central Google Scholar
Annisa, A., Prasetyo, I., Swantomo, D. & Ariyanto, T. Surface modification of nanoporous carbon using gamma irradiation treatment as supercapacitor material. AIP Conf. Proc. 2349(1), 020007. https://doi.org/10.1063/5.0052360 (2021).
Article CAS Google Scholar
Maxwell, A. S., Wang, Y. & Tomlins, P. E. On the use of gamma radiation to change the characteristics of porous Poly(caprolactone) tissue scaffolds. Int. J. Polym. Mater. Polym. Biomater. 63(3), 123–129. https://doi.org/10.1080/00914037.2013.769257 (2014).
Article CAS Google Scholar
Jiang, Y. & Liu, J. Definitions of pseudocapacitive materials: A brief review. Energy Environ. Mater. 2(1), 30–37. https://doi.org/10.1002/eem2.12028 (2019).
Article MathSciNet Google Scholar
Abbas, Q., Raza, R., Shabbir, I. & Olabi, A. G. Heteroatom doped high porosity carbon nanomaterials as electrodes for energy storage in electrochemical capacitors: A review. J. Sci. Adv. Mater. Devices 4(3), 341–352. https://doi.org/10.1016/j.jsamd.2019.07.007 (2019).
Article Google Scholar
Wang, G., Oswald, S., Löffler, M., Müllen, K. & Feng, X. Beyond activated carbon: graphite-cathode-derived li-ion pseudocapacitors with high energy and high power densities. Adv. Mater. 31(14), 1807712. https://doi.org/10.1002/adma.201807712 (2019).
Article CAS Google Scholar
Kruse, A. & Zevaco, T. A. Properties of hydrochar as function of feedstock, reaction conditions and post-treatment. Energies https://doi.org/10.3390/en11030674 (2018).
Article Google Scholar
Khan, T. A. et al. Hydrothermal carbonization of lignocellulosic biomass for carbon rich material preparation: A review. Biomass Bioenergy 130, 105384. https://doi.org/10.1016/j.biombioe.2019.105384 (2019).
Article CAS Google Scholar
Reza, M. T., Rottler, E., Herklotz, L. & Wirth, B. Hydrothermal carbonization (HTC) of wheat straw: Influence of feedwater pH prepared by acetic acid and potassium hydroxide. Bioresour. Technol. 182, 336–344. https://doi.org/10.1016/j.biortech.2015.02.024 (2015).
Article CAS PubMed Google Scholar
Coates, J. Interpretation of Infrared Spectra, A Practical Approach (Encyclopedia of Analytical Chemistry) (Wiley, 2006).
Manna, K., Srivastava, S. K. & Mittal, V. Role of enhanced hydrogen bonding of selectively reduced graphite oxide in fabrication of Poly(vinyl alcohol) nanocomposites in water as EMI shielding material. J. Phys. Chem. C 120(30), 17011–17023. https://doi.org/10.1021/acs.jpcc.6b03356 (2016).
Article CAS Google Scholar
Zhao, Y. & Zhang, X. In situ activation graphitization to fabricate hierarchical porous graphitic carbon for supercapacitor. Sci. Rep. 11(1), 6825. https://doi.org/10.1038/s41598-021-85661-0 (2021).
Article ADS CAS PubMed PubMed Central Google Scholar
Wang, H. et al. Control of the interface graphitized/amorphous carbon of biomass-derived carbon microspheres for symmetric supercapacitors. Nanoscale Adv. 3(16), 4858–4865. https://doi.org/10.1039/D1NA00262G (2021).
Article ADS CAS PubMed PubMed Central Google Scholar
Zou, J. et al. High-performance supercapacitors based on hierarchically porous carbons with a three-dimensional conductive network structure. Dalton Trans. 48(16), 5271–5284. https://doi.org/10.1039/C9DT00261H (2019).
Article CAS PubMed Google Scholar
Qi, F. et al. Graphitization induced by KOH etching for the fabrication of hierarchical porous graphitic carbon sheets for high performance supercapacitors. J. Mater. Chem. A 6(29), 14170–14177. https://doi.org/10.1039/C8TA01186A (2018).
Article CAS Google Scholar
Ferrari, A. C. & Robertson, J. Interpretation of Raman spectra of disordered and amorphous carbon. Phys. Rev. B 61(20), 14095–14107. https://doi.org/10.1103/PhysRevB.61.14095 (2000).
Article ADS CAS Google Scholar
Jorio, A. et al. Measuring disorder in graphene with the G and D bands. Phys. Status Solidi (b) 247(11–12), 2980–2982. https://doi.org/10.1002/pssb.201000247 (2010).
Article ADS CAS Google Scholar
Xing, T. et al. Disorder in ball-milled graphite revealed by Raman spectroscopy. Carbon 57, 515–519. https://doi.org/10.1016/j.carbon.2013.02.029 (2013).
Article CAS Google Scholar
Ni, Z., Wang, Y., Yu, T. & Shen, Z. Raman spectroscopy and imaging of graphene. Nano Res. 1(4), 273–291. https://doi.org/10.1007/s12274-008-8036-1 (2008).
Article CAS Google Scholar
Elgrishi, N. et al. A practical beginner’s guide to cyclic voltammetry. J. Chem. Educ. 95(2), 197–206. https://doi.org/10.1021/acs.jchemed.7b00361 (2018).
Article CAS Google Scholar
Heimböckel, R., Hoffmann, F. & Fröba, M. Insights into the influence of the pore size and surface area of activated carbons on the energy storage of electric double layer capacitors with a new potentially universally applicable capacitor model. Phys. Chem. Chem. Phys. 21(6), 3122–3133. https://doi.org/10.1039/C8CP06443A (2019).
Article PubMed Google Scholar
Wang, H. & Pilon, L. Physical interpretation of cyclic voltammetry for measuring electric double layer capacitances. Electrochim. Acta 64, 130–139. https://doi.org/10.1016/j.electacta.2011.12.118 (2012).
Article CAS Google Scholar
Braghiroli, F. L. et al. Electrochemical performances of hydrothermal tannin-based carbons doped with nitrogen. Ind. Crops Products 70, 332–340. https://doi.org/10.1016/j.indcrop.2015.03.046 (2015).
Article CAS Google Scholar
Rezaie, E., Hajalilou, A., Su, Y. Perovskites for supercapacitors, in Handbook of Supercapacitor Materials, 131–185 (2021).
Chodankar, N. R. et al. True meaning of pseudocapacitors and their performance metrics: asymmetric versus hybrid supercapacitors. Small 16(37), 2002806. https://doi.org/10.1002/smll.202002806 (2020).
Article CAS Google Scholar
Hsia, B., Kim, M. S., Carraro, C. & Maboudian, R. Cycling characteristics of high energy density, electrochemically activated porous-carbon supercapacitor electrodes in aqueous electrolytes. J. Mater. Chem. A 1(35), 10518–10523. https://doi.org/10.1039/C3TA11670K (2013).
Article CAS Google Scholar
Abdul Wahab, Y. et al. Super capacitors in various dimensionalities: Applications and recent advancements. In Encyclopedia of Energy Storage (ed. Cabeza, L. F.) 682–691 (Elsevier, 2022).
Chapter Google Scholar
Shao , H. , Lin , Z. , Xu , K. , Tavern , P.-L.& Simon , P. Electrochemical study of pseudocapacitive behavior of Ti3C2Tx MXene material in aqueous electrolytes .Energy Storage Mater.18 , 456–461.https://doi.org/10.1016/j.ensm.2018.12.017 (2019).
Article Google Scholar
Rajkumar, M., Hsu, C.-T., Wu, T.-H., Chen, M.-G. & Hu, C.-C. Advanced materials for aqueous supercapacitors in the asymmetric design. Prog. Nat. Sci. Mater. Int. 25(6), 527–544. https://doi.org/10.1016/j.pnsc.2015.11.012 (2015).
Article CAS Google Scholar
Kazemi, S. H., Tabibpour, M., Kiani, M. A. & Kazemi, H. An advanced asymmetric supercapacitor based on a binder-free electrode fabricated from ultrathin CoMoO4 nano-dandelions. RSC Adv. 6(75), 71156–71164. https://doi.org/10.1039/C6RA05703A (2016).
Article ADS CAS Google Scholar
Samiei, E., Mohammadi, S. & Torkzadeh-Mahani, M. Effect of gamma-irradiation on electrochemical properties of ZnCo2O4-rGO for supercapacitor application. Diam. Relat. Mater. 127, 109157. https://doi.org/10.1016/j.diamond.2022.109157 (2022).
Article ADS CAS Google Scholar
Mohd Nor, N. S. et al. Influence of gamma irradiation exposure on the performance of supercapacitor electrodes made from oil palm empty fruit bunches. Energy 79, 183–194. https://doi.org/10.1016/j.energy.2014.11.002 (2015).
Article CAS Google Scholar
Fang, Y., Zhang, Q. & Cui, L. Recent progress of mesoporous materials for high performance supercapacitors. Microporous Mesoporous Mater. 314, 110870. https://doi.org/10.1016/j.micromeso.2020.110870 (2021).
Article CAS Google Scholar
Xie, M., Yang, J., Liang, J., Guo, X. & Ding, W. In situ hydrothermal deposition as an efficient catalyst supporting method towards low-temperature graphitization of amorphous carbon. Carbon 77, 215–225. https://doi.org/10.1016/j.carbon.2014.05.024 (2014).
Article CAS Google Scholar
Chen, Q. et al. Biomass-derived porous graphitic carbon materials for energy and environmental applications. J. Mater. Chem. A 8(12), 5773–5811. https://doi.org/10.1039/C9TA11618D (2020).
Article ADS CAS Google Scholar
Sivachidambaram, M. et al. Preparation and characterization of activated carbon derived from the Borassus flabellifer flower as an electrode material for supercapacitor applications. New J. Chem. 41(10), 3939–3949. https://doi.org/10.1039/C6NJ03867K (2017).
Article CAS Google Scholar
Zheng, L.-H., Chen, M.-H., Liang, S.-X. & Lü, Q.-F. Oxygen-rich hierarchical porous carbon derived from biomass waste-kapok flower for supercapacitor electrode. Diam. Relat. Mater. 113, 108267. https://doi.org/10.1016/j.diamond.2021.108267 (2021).
Article ADS CAS Google Scholar
Li, X. & Wu, G. Porous carbon from corn flour prepared by H3PO4 carbonization combined with KOH activation for supercapacitors. J. Power Energy Eng. 9(8), 8. https://doi.org/10.4236/jpee.2021.98002 (2021).
Article Google Scholar
Yu, K., Zhu, H., Qi, H. & Liang, C. High surface area carbon materials derived from corn stalk core as electrode for supercapacitor. Diam. Relat. Mater. 88, 18–22. https://doi.org/10.1016/j.diamond.2018.06.018 (2018).
Article ADS CAS Google Scholar
Okonkwo, C. A. et al. Liquid nitrogen-controlled direct pyrolysis/KOH activation mediated micro-mesoporous carbon synthesis from castor shell for enhanced performance of supercapacitor electrode. Biomass Convers. Biorefinery https://doi.org/10.1007/s13399-021-01356-6 (2021).
Article Google Scholar
Yuan, X., Xiao, J., Yılmaz, M., Zhang, T. C. & Yuan, S. N, P Co-doped porous biochar derived from cornstalk for high performance CO2 adsorption and electrochemical energy storage. Sep. Purif. Technol. 299, 121719. https://doi.org/10.1016/j.seppur.2022.121719 (2022).
Article CAS Google Scholar
This work was supported by Thailand Science Research and Innovation (TSRI), Thailand Institute of Nuclear Technology through TINT to University program, and the Development and Promotion of Science and Technology Talents Project (DPST).
Department of Chemistry, School of Science, Walailak University, Tha Sala, Nakhon Si Thammarat, 80160, Thailand
Nurulsafeelanaria Benwannamas & Kotchaphan Kanjana
Functional Materials and Nanotechnology Center of Excellence, Walailak University, Tha Sala, Nakhon Si Thammarat, 80160, Thailand
Nurulsafeelanaria Benwannamas & Kotchaphan Kanjana
Thailand Institute of Nuclear Technology, Ongkharak, Nakhon Nayok, 26120, Thailand
Department of Chemistry and Chemical Processing Technologies, Bahçe Vocational School, Osmaniye Korkut Ata University, 80000, Osmaniye, Turkey
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
K.K. developed the conceptual framework of the research, conducted data analysis, wrote and edited the main manuscript text. N.B. performed AC synthesis, FTIR and electrochemical measurements, and drafted the manuscript. T.S. performed Raman spectroscopy analysis and M.Y. added discussion for electrochemical measurements. All authors reviewed the manuscript.
The authors declare no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
Benwannamas, N., Sangtawesin, T., Yilmaz, M. et al. Gamma-induced interconnected networks in microporous activated carbons from palm petiole under NaNO3 oxidizing environment towards high-performance electric double layer capacitors (EDLCs). Sci Rep 13, 12887 (2023). https://doi.org/10.1038/s41598-023-40176-8
DOI: https://doi.org/10.1038/s41598-023-40176-8
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.
Scientific Reports (Sci Rep) ISSN 2045-2322 (online)
Ultra Capacitor Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.